Название: | Physicomechanical properties of ultrahigh temperature heteromodulus ceramics based on group 4 transition metal carbides |
Автор: | Shabalin, I. L. Wang, Y. Krynkin, A. V. Umnova, O. V. Vishnyakov, V. M. Shabalin, L. I. Churkin, V. K. |
Дата публикации: | 2010 |
Издатель: | Informa UK Limited |
Аннотация: | Highly densified TiC, ZrC and HfC based ultrahigh temperature heteromodulus ceramics (HMC), containing 10-50 vol.-% of low modulus phase in the form of particulate graphite, were prepared by hot pressing at 2700°C and 12 MPa in argon atmosphere. The microstructure, elastic characteristics, flexural and compressive static strength, fracture toughness, impact resistance, hardness and thermal expansion were investigated and compared with those available in earlier works for clear understanding the composition-property correlations and anisotropy of this type of HMC composites. Different thermal shock resistant parameters for the HMC were calculated on the basis of obtained experimental data. A new principle of optimum materials design for the compositions in the refractory carbide-graphite systems is exemplified by the TiC-C HMC materials. © 2010 Institute of Materials, Minerals and Mining. |
Ключевые слова: | CARBIDES CARBON COMPOSITES HETEROMODULUS CERAMICS MECHANICAL PROPERTIES ARGON ATMOSPHERES COMPOSITES ELASTIC CHARACTERISTIC EXPERIMENTAL DATA GROUP 4 HETERO-MODULUS CERAMICS LOW MODULUS MATERIALS DESIGN PHYSICOMECHANICAL PROPERTIES REFRACTORY CARBIDES STATIC STRENGTH THERMAL SHOCK RESISTANT TRANSITION METAL CARBIDE ULTRAHIGH TEMPERATURE ARGON CERAMIC MATERIALS COMPRESSIVE STRENGTH FRACTURE TOUGHNESS GRAPHITE HOT PRESSING IMPACT RESISTANCE THERMAL EXPANSION TITANIUM CARBIDE TRANSITION METALS ZIRCONIUM COMPOUNDS MECHANICAL PROPERTIES |
ISSN: | 1743-6753 1743-6761 |
DOI: | 10.1179/174367509X12535211569431 |
SCOPUS: | 77957596020 |
WoS: | 000282141000007 |
Располагается в коллекциях: | Научные публикации, проиндексированные в SCOPUS и WoS |
Файлы этого ресурса:
Нет файлов, ассоциированных с этим ресурсом.
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.